2011
AMS QQ-A-225/3 / AlCu6BiPb / 2011 / T4
Chemical Properties | % Value |
Silicon (Si) | 0,40 Max |
Copper (Cu) | 5,00 - 6,00 |
Lead (Pb) | 0,20 - 0,60 |
Iron (Fe) | 0,70 Max |
Zinc (Zn) | 0,00 - 0,30 |
Aluminium (Al) | Balance |
Physical Properties | Value |
Density | 2.82 g/cm³ |
Melting Point | 540 °C |
Thermal Expansion | 22,9 x 10^-6 /K |
Modulus of Elasticity | 70 GPa |
Thermal Conductivity | 150 W/m.K |
Electrical Resistivity | %39 |
Mechanical Properties | Value |
Proof Strength | 140 MPa |
Yield Strength | 310 MPa |
Elongation A50 mm | %18 |
Modulus of Elasticity | 70 GPa |
Aluminium alloy 2011 is a high mechanical strength alloy that machines exceptionally well. Often called a Free Machining Alloy or ‘FMA’ it is well suited to use in automatic lathes.
ALLOY DESIGNATIONS
Aluminium alloy 2011, AMS QQ-A-225/3 is covered by Standard BS EN 2100 and has similarities to the following standard designations and specifications:
2011, ISO AlCu6BiPb, 3.1655
UNS A92011, BS FC1
TEMPER TYPES
The most common tempers for 2011 aluminium are:
- O - Soft
- T3 - Solution heat treated, cold worked and naturally aged
- T4 - Solution heat treated and naturaly aged to a substantially stable condition.
- T8 - Solution heat-treated, cold worked and then artificially aged.
- T451 - Solution heat-treated, stress-relieved by controlled stretching and then artificially overaged (between T73 and T76). The products receive no further straightening after stretching.
SUPPLIED FORMS
2011 aluminium is supplied in round bar.
- Round Bar
Mechanical Properties | |||
Thickness (mm) | Proof Strength (Min.) | Yield Strength (Min.) | Elongation A50 mm % |
Up to & incl. 60 | 125 | 275 | %14 |