1100
AMS 4062 / Al99.0Cu / 1100 / H14
化学性质 | % 值 |
Silicon (Si) | 0,00 - 0,95 |
Manganese (Mn) | 0,00 - 0,05 |
Copper (Cu) | 0,05 - 0,20 |
Iron (Fe) | 0,00 - 0,95 |
Zinc (Zn) | 0,00 - 0,1 |
Aluminium (Al) | Balance |
物理特性 | 值 |
Density | 2,71 g/cm³ |
Melting Point | 643 °C |
Thermal Expansion | 23.6 x 10^-6 /K |
Modulus of Elasticity | 69 GPa |
Thermal Conductivity | 220 W/m.K |
Electrical Resistivity | %58 IACS |
机械性能 | 值 |
Proof Strength | 120 MPa |
Yield Strength | 130 MPa |
Shear Strength | 76 MPa |
Elongation A50 mm | %9 |
Modulus of Elasticity | 69 GPa |
Low strength aluminum alloy has excellent corrosion resistance and satisfactory anodizing and conversion coating finishing characteristics. It is unmatched by any other commercial aluminum alloy in workability.
ALLOY DESIGNATIONS
Aluminium alloy 1100, AMS QQ-A-250/1 has s imilarities to the following standard designations and specifications ;
AA 1100, AMS 4001
ISO Al99Cu
TEMPER TYPES
The most common tempers for 1100 aluminium are:
- O - Soft
- F
- H14 - Strain-hardened - 1/2 hard.
- H18 - Strain-hardened - 4/4 hard (fully hardened).
SUPPLIED FORMS
1100 aluminium is supplied in in plate, sheet, extrusions and bar.
- Plate
- Sheet
- Bar
- Extrusions