EN AW / AlMgSi / 6060 / T6
| Chemical Properties | % Value |
| Silicon (Si) | 0,40 - 0,80 |
| Chromium (Cr) | 0,04 - 0,35 |
| Manganese (Mn) | 0,00 - 0,15 |
| Magnesium (Mg) | 0,80 - 1,20 |
| Copper (Cu) | 0,15 - 0,40 |
| Titanium (Ti) | 0,00 - 0,15 |
| Iron (Fe) | 0,00 - 0,70 |
| Zinc (Zn) | 0,00 - 0,25 |
| Aluminium (Al) | Balance |
| Physical Properties | Value |
| Density | 2,70 g/cm³ |
| Melting Point | 582 °C |
| Thermal Expansion | 23.4 x10^-6 /K |
| Modulus of Elasticity | 69 GPa |
| Thermal Conductivity | 170 W/m.K |
| Electrical Resistivity | %43 IACS |
| Mechanical Properties | Value |
| Proof Strength | 310 MPa |
| Yield Strength | 270 MPa |
| Shear Strength | 207 MPa |
| Elongation A50 mm | %15 |
| Modulus of Elasticity | 69 GPa |
6060 T6 is A medium strength aerospace aluminium alloy with, depending upon temper, Yield Strength of up to 35 ksi (240 MPa) and Tensile Strength of 42 ksi (290 MPa)
ALLOY DESIGNATIONS
EN AW 6060 has s imilarities to the following standard designations and specifications ;
Alloy 6060, UNS A96060, ASTM B209 ASTM B221 ASTM B211
EN 4213, 3.3206
TEMPER TYPES
6060 is supplied in a wide range of tempers:
- O - Soft
- T4 - Solution heat treated and naturaly aged to a substantially stable condition
- T5 - Cooled from an elevated temperature shaping process and artificially aged
- T6 - Solution heat treated and artificially aged
- T66 - Solution heat treated then artificially aged by the user
- T6511 - Solution heat treated, stress relieved by stretching then artificially aged
SUPPLIED FORMS
6060 is supplied in plate, bar, round bar, tube, extrusıon and sheet.
- Plate
- Sheet
- Round Bar / Bar
- Tube / Extrusion