7079
ASTM B221 / AlZn4Mg3Cu / 7079 / O
Chemical Properties | % Value |
Silicon (Si) | 0,00 - 0,40 |
Chromium (Cr) | 0,18 - 0,28 |
Manganese (Mn) | 0,00 - 0,30 |
Magnesium (Mg) | 2,10 - 2,90 |
Copper (Cu) | 1,20 - 2,00 |
Titanium (Ti) | 0,00 - 0,20 |
Iron (Fe) | 0,00 - 0,50 |
Zinc (Zn) | 5,10 - 6,10 |
Aluminium (Al) | Balance |
Physical Properties | Value |
Density | 2.81 g/cm³ |
Melting Point | 635 °C |
Thermal Expansion | 23.5 x 10^-6 /K |
Modulus of Elasticity | 72 GPa |
Thermal Conductivity | 134-160 W/m.K |
Electrical Resistivity | %40 IACS |
A high strength aerospace aluminium alloy with, depending on temper.
ALLOY DESIGNATIONS
AMS QQ-A-250/12, 7075 has similarities to the following standard designations and specifications ;
Alloy 7075, UNS A97075, ASTM B209
AMS 4045, AlZn5.5MgCu, DIN 3.4364
AIR 9048.680, BS L95, EN 2126
TEMPER TYPES
7075 is supplied in a wide range of tempers:
- O - Soft
- F - As fabricated
- T6 - Solution heat-treated and then artificially aged.
- T62 - Solution heat-treated and then artificially aged. Applies to test material heat-treated from annealed or F temper or to products heat-treated from any temper by the user.
- T651 - Solution heat-treated, stress-relieved by controlled stretching (permanent set 0.5% to 3% for sheet, 1.5% to 3% for plate, 1% to 3% for rolled or cold-finished rod and bar, 1% to 5% for hand or ring forging and rolled ring) and then artificially aged. The products receive no further straightening after stretching.
- T6510 - Solution heat-treated, stress-relieved by controlled stretching (permanent set 1% to 3% for extruded rod, bar, shapes and tube, 0.5% to 3% for drawn tube) and then artificially aged. The products receive no further straightening after stretching.
- T6511 - Same as T6510 except that minor straightening is allowed after stretching to comply with standard tolerances
- T73 - Solution heat-treated and then artificially overaged in order to achieve the best stress corrosion resistance.
- T7351 - Solution heat-treated, stress-relieved by controlled stretching (permanent set 0.5% to 3% for sheet, 1.5% to 3% for plate, 1% to 3% for rolled or cold-finished rod and bar, 1% to 5% for hand or ring forging and rolled ring) and then artificially overaged in order to achieve the best stress corrosion resistance. The products receive no further straightening after stretching.
- T73510 - Solution heat-treated, stress-relieved by controlled stretching (permanent set 1% to 3% for extruded rod, bar, shapes and tube, 0.5% to 3% for drawn tube) and then artificially overaged in order to achieve the best stress corrosion resistance. The products receive no further straightening after stretching
- T73511 - Same as T73510 except that minor straightening is allowed after stretching to comply with standard tolerances.
- T76 - Solution heat-treated and then artificially overaged in order to achieve a good exfoliation corrosion resistance.
- T76511 - Solution heat-treated, stress-relieved by controlled stretching (permanent set 1% to 3% for extruded rod, bar, shapes and tube, 0.5% to 3% for drawn tube) and then artificially overaged in order to achieve a good exfoli-ation corrosion resistance. The products receive no further straightening after stretching, except that minor straightening is allowed after stretching to comply with standard tolerances.
SUPPLIED FORMS
7075 is supplied in plate, sheet, bar and extrusions.
- Plate
- Sheet
- Round Bar / Bar
- Tube / Extrusions
DELIVERY:
Mechanical Properties | |||
Thickness (mm) | Proof Strength (Min.) | Yield Strength (Min.) | Elongation A50 mm % |
Over 6.3 up to & incl. 12.6 | 462 MPa | 538 MPa | %9 |
Over 12,7 up to & incl. 25,4 | 469 MPa | 538 MPa | %7 |
Over 25,4 up to & incl. 50,8 | 462 MPa | 531 MPa | %6 |
Over 50,8 up to & incl. 63,5 | 441 MPa | 524 MPa | %6 |
Over 63,5 up to & incl. 76,2 | 421 MPa | 496 MPa | %5 |
Over 76,2 up to & incl. 88,9 | 400 MPa | 490 MPa | %5 |
Over 88,9 up to & incl. 101,6 | 372 MPa | 462 MPa | %3 |