7475
EN AW / AlZn5.5MgCu / 7475 / T651
Chemical Properties | % Value |
Silicon (Si) | 0,00 - 0,10 |
Chromium (Cr) | 0,18 - 0,25 |
Manganese (Mn) | 0,00 - 0,06 |
Magnesium (Mg) | 1,90 - 2,60 |
Copper (Cu) | 1,20 - 1,90 |
Titanium (Ti) | 0,00 - 0,06 |
Iron (Fe) | 0,00 - 0,12 |
Zinc (Zn) | 5,2 - 6,20 |
Aluminium (Al) | Balance |
Physical Properties | Value |
Density | 2,81 g/cm³ |
Melting Point | 477 °C |
Thermal Expansion | 23 x 10^-6 /K |
Modulus of Elasticity | 71,7 GPa |
Thermal Conductivity | 138 W/m.K |
Electrical Resistivity | %34 IACS |
Mechanical Properties | Value |
Proof Strength | 510 MPa |
Yield Strength | 586 MPa |
Shear Strength | 350 MPa |
Elongation A50 mm | %12 |
Modulus of Elasticity | 71,7 GPa |
7475 T651 aluminum alloy; It is a very high strength material which provides superior toughness against the spread of fatigue crack and fracture. It has been developed particularly in a controlled way for sheet and plate applications. The 7475 alloy is 40 percent higher than 7075 T651 alloy for in typical fracture toughness at the same temparatures. Corrosion resistance and fatigue behavior of 7475 alloy; Much better than mostly preferred high strength aerospace alloys such as 7075, 7050 and 2024. In some cases it is incomparable.
Referans Metal is the first company which exported 7475 T651 plates in AMS 4090 standards from Turkey in 2007. In addition, Referans Metal is the first and only company that makes the first injection mold applications in Hadımköy and Gebze for the machine-mold industry in Turkey.
Plate as; AMS 4090
Alloy 7475, UNS A97475, AlZn5.5MgCu
MINIMUM FRACTURE TOUGHNESS VALUES FOR 7475 T651:
KIc: ksi√in.(MPa√m)
Temper Thickness L-T T-L
T651 1.250-1.500 in. 30.0 (33.0) 28.0 (30.8)
(31.75-38.10 mm)
Choosing Factors for 7475 T651:
- Strength: Very good
- Machining: Fair
- Weldability: Low
- Formability: Poor
- Corrosion Resistance: Normal
- Heat Treating:Yes
TEMPER TYPES
EN AW 7475 is supplied in the following heat treatment types:
- T61
- T651
- T7351
- T76
- T761
- T7651
Some Well-Known Applications for 7475 T651:
In aircraft parts, especially in the construction of wing parts and connecting devices.
Airframe.
As an interdepartmental protective set in closed systems under high dynamic force.
- Plate
- Sheet
Mechanical Properties | |||
Thickness (mm) | Proof Strength (Min.) | Yield Strength (Min.) | Elongation A50 mm % |
over 6.35 up to & incl. 12.67 | 462 MPa | 538 MPa | 10 |
over 25.42 up to & incl. 38.10 | 469 MPa | 542 MPa | 9 |