AMS QQ-A-225/3 / AlCu6BiPb / 2011 / T8
Chemical Properties | % Value |
Silicon (Si) | 0,40 Max |
Copper (Cu) | 5,00 - 6,00 |
Lead (Pb) | 0,20 - 0,60 |
Iron (Fe) | 0,70 Max |
Zinc (Zn) | 0,00 - 0,30 |
Nickel (Ni) | 0,00 - 0,20 |
Aluminium (Al) | Balance |
Physical Properties | Value |
Density | 2.82 g/cm³ |
Melting Point | 540 °C |
Thermal Expansion | 22.9 x 10^-6 /K |
Modulus of Elasticity | 70 GPa |
Thermal Conductivity | 170 W/m.K |
Electrical Resistivity | %46 IACS |
Mechanical Properties | Value |
Proof Strength | 310 MPa |
Yield Strength | 420 MPa |
Shear Strength | 240 MPa |
Elongation A50 mm | %12 |
Modulus of Elasticity | 70 GPa |
5L36 - 1050A has excellent characteristic properties: Very good atmospheric corrosion resistance. Very good workability. High thermal and electrical conductivity (preferred alloy 1350). Attractive appearance, high reflectivity. Suitable for decorative anodising. Very good weldability with low mechanical properties.
ALLOY DESIGNATIONS
Aluminium alloy 5L36 - 1050A is covered by Standard BS EN 5L36 (1985)
TEMPER TYPES
The most common tempers for 5L36 - 1050A aluminium wire / rivet stock is as-drawn
SUPPLIED FORMS
L36-1050A aluminium is supplied in Wire as rivet stock.
- Round Bar
- Wire
Mechanical Properties | |||
Thickness (mm) | Proof Strength (Min.) | Yield Strength (Min.) | Elongation A50 mm % |
Over 3.17 up to & incl. 82.5 | 275 MPa | 310 MPa | %10 |