7150
AMS 4306 / AlZn6CuMgZr / 7150 / T6151
Chemical Properties | % Value |
Silicon (Si) | 0,00 - 0,12 |
Chromium (Cr) | 0,00 - 0,04 |
Manganese (Mn) | 0,00 - 0,10 |
Magnesium (Mg) | 2,00 - 2,70 |
Copper (Cu) | 1,9 - 2,50 |
Titanium (Ti) | 0,00 - 0,06 |
Iron (Fe) | 0,00 - 0,15 |
Zinc (Zn) | 5,90 - 6,90 |
Aluminium (Al) | Balance |
Titanium + Zirconium (Ti+Zr) | 0,08 - 0,15 |
Physical Properties | Value |
Density | 2,86 g/cm³ |
Mechanical Properties | Value |
Proof Strength | 565 to 614 MPa |
Yield Strength | 593 to 648 MPa |
Elongation A50 mm | %9 to 12 |
Alloy 7150 is the highest strength aluminum plate alloy/temper currently available for commercial aircraft applications.
ALLOY DESIGNATIONS
AMS 4306, 7150 has similarities to the following standard designations and specifications ;
Alloy 7150, UNS A97150, ASTM B209
AMS 4306, AlZn6Mg2Cu
TEMPER TYPES
7150 is supplied in a wide range of tempers:
- T6151 - Solution heat-treated, stress-relieved by controlled stretching (permanent set 0.5% to 3% for sheet, 1.5% to 3% for plate) and then artificially aged in underageing conditions to improve formability. The products receive no further straightening after stretching.
- T61511 - Solution heat-treated, stress-relieved by controlled stretching (permanent set 0.5% to 3% for sheet, 1.5% to 3% for plate) and then artificially aged in underageing conditions to improve formability. The products receive no further straightening after stretching except that minor straightening is allowed after stretching to comply with standard tolerances.
- T7751 - Solution heat-treated, stress-relieved by controlled stretching and then artificially overaged in order to achieve a good exfoliation corrosion resistance. The products recieve no further straightening after stretching.
- T77511 - Solution heat-treated, stress-relieved by controlled stretching and then artificially overaged in order to achieve a good exfoliation corrosion resistance. The products recieve no further straightening after stretching.except that minor straightening is allowed after stretching to comply with standard tolerances.
SUPPLIED FORMS
7075 is supplied in plate, and extrusions.
- Plate
- Tube / Extrusions
DELIVERY:
Mechanical Properties | |||
Thickness (mm) | Proof Strength (Min.) | Yield Strength (Min.) | Elongation A50 mm % |
25,4 mm | 565 MPa | 607 MPa | %11 |