2014

EN AW / AlCu4SiMg / 2014 / T4

Chemical Properties % Value
Silicon (Si)0,50 - 1,20
Chromium (Cr)0,00 - 0,10
Manganese (Mn)0,40 - 1,20
Magnesium (Mg)0,20 - 0,80
Copper (Cu)3,90 - 5,00
Titanium (Ti)0,00 - 0,15
Iron (Fe)0,00 - 0,70
Zinc (Zn)0,00 - 0,25
Aluminium (Al)Balance
Physical Properties Value
Density2.80 g/cm³
Melting Point507 °C
Thermal Expansion22.7 x 10^-6 /K
Modulus of Elasticity73 GPa
Thermal Conductivity130 W/m.K
Electrical Resistivity%34 IACS
Mechanical Properties Value
Proof Strength280 MPa
Yield Strength430 MPa
Shear Strength260 MPa
Elongation A50 mm%17
Modulus of Elasticity73 GPa

High strength structural components for aircraft , military vehicles and bridges, weapons manufacture, structural applications. 

 

ALLOY DESIGNATIONS

Aluminium alloy 2014 / 2014A is covered by Standard BS EN 2100 and has similarities to the following standard designations and specifications:

Alloy 2014, UNS A92014, ASTM B209

DIN AlCu4SiMg, 3.1255

 

TEMPER TYPES

The most common tempers for 2014 / 2014A aluminium are:

  • O   - Soft
  • T3 - Solution heat treated, cold worked and naturally aged
  • T4 - Solution heat treated and naturaly aged to a substantially stable condition
  • T6 - Solution heat treated and artificially aged
  • T651 - Solution heat treated, stress relieved by stretching then artificially aged

 

SUPPLIED FORMS

AMS 4029 aluminium is supplied in Plate.

  • Plate