7010
EN AW / AlZn6MgCu / 7010 / T7651
Chemical Properties | % Value |
Silicon (Si) | 0,00 - 0,12 |
Chromium (Cr) | 0,00 - 0,05 |
Manganese (Mn) | 0,00 - 0,10 |
Magnesium (Mg) | 2,10 - 2,60 |
Copper (Cu) | 1,50 - 2,00 |
Titanium (Ti) | 0,00 - 0,06 |
Iron (Fe) | 0,00 - 0,15 |
Zinc (Zn) | 5,70 - 6,70 |
Aluminium (Al) | Balance |
Physical Properties | Value |
Density | 2.81 g/cm³ |
Melting Point | 475 °C |
Thermal Expansion | 23,7 x 10^-6 /K |
Modulus of Elasticity | 71 GPa |
Thermal Conductivity | 150 W/m.K |
Mechanical Properties | Value |
Proof Strength | 490 MPa |
Yield Strength | 570 MPa |
Elongation A50 mm | %8 |
Modulus of Elasticity | 71 GPa |
Alloy 7010 has been represented as being a high strength/high toughness, and stress corrosion cracking resistant aluminum alloy.
ALLOY DESIGNATIONS
Aluminium alloy EN AW 7010 has similarities to the following standard designations and specifications ;
Alloy 7010, UNS A97010, ASTM B209
DIN AlZn6MgCu
TEMPER TYPES
AMS 4204, 7010 is supplied in a wide range of tempers:
- T7351 - Solution heat treatment then specially artifically aged for resistance to stress corrosion.
- T7451 - Solution heat-treated, stress-relieved by controlled stretching . The products receive no further straightening after stretching.
- T7651 - Solution heat-treated, stress-relieved by controlled stretching (permanent set 0.5% to 3% for sheet, 1.5% to 3% for plate, 1% to 3% for rolled or cold-finished rod and bar, 1% to 5% for hand or ring forging and rolled ring) and then artificially overaged in order to achieve a good exfoliation corrosion resistance. The products recieve no further straightening after stretching.
SUPPLIED FORMS
7010 is supplied in plate and bar.
- Plate
- Round Bar / Bar
DELIVERY: