1100
EN AW / Al99Cu / 1100 / O
Chemical Properties | % Value |
Silicon (Si) | 0,00 - 0,95 |
Manganese (Mn) | 0,00 - 0,05 |
Copper (Cu) | 0,05 - 0,20 |
Iron (Fe) | 0,00 - 0,95 |
Zinc (Zn) | 0,00 - 0,10 |
Aluminium (Al) | Balance |
Physical Properties | Value |
Density | 2,71 g/cm³ |
Melting Point | 643 °C |
Thermal Expansion | 24.5 x 10^-6 /K |
Modulus of Elasticity | 69 GPa |
Thermal Conductivity | 220 W/m.K |
Electrical Resistivity | %58 IACS |
Mechanical Properties | Value |
Proof Strength | 28 MPa |
Yield Strength | 90 MPa |
Shear Strength | 62 MPa |
Elongation A50 mm | %35 |
Modulus of Elasticity | 69 GPa |
High strength structural components for aircraft , military vehicles and bridges, weapons manufacture, structural applications.
ALLOY DESIGNATIONS
Aluminium alloy 2014 / 2014A is covered by Standard BS EN 2100 and has similarities to the following standard designations and specifications:
2014 / 2014A , AMS 4029, ISO AlCu4SiMg, DIN AlCuSiMn, UNS A92014, BS L93
TEMPER TYPES
The most common tempers for 2014 / 2014A aluminium are:
- O - Soft
- T3 - Solution heat treated, cold worked and naturally aged
- T4 - Solution heat treated and naturaly aged to a substantially stable condition
- T6 - Solution heat treated and artificially aged
- T651 - Solution heat treated, stress relieved by stretching then artificially aged
SUPPLIED FORMS
AMS 4029 aluminium is supplied in Plate.
- Plate
DELIVERY: