6061
AMS 4150 / AlMg1SiCu / 6061 / T6
| 化学性质 | % 值 |
| Silicon (Si) | 0,40 - 0,80 |
| Chromium (Cr) | 0,04 - 0,35 |
| Manganese (Mn) | 0,00 - 0,15 |
| Magnesium (Mg) | 0,80 - 1,20 |
| Copper (Cu) | 0,15 - 0,40 |
| Titanium (Ti) | 0,00 - 0,15 |
| Iron (Fe) | 0,00 - 0,70 |
| Zinc (Zn) | 0,00 - 0,25 |
| Aluminium (Al) | Balance |
| 物理特性 | 值 |
| Density | 2.70 g/cm³ |
| Melting Point | 582 °C |
| Thermal Expansion | 23.6 µm/m.°C |
| Modulus of Elasticity | 69 GPa |
| Thermal Conductivity | 167 W/m.K |
| Electrical Resistivity | %43 IACS |
| 机械性能 | 值 |
| Proof Strength | 276 MPa |
| Yield Strength | 310 MPa |
| Shear Strength | 207 MPa |
| Elongation A50 mm | 15% |
| Hardness | 95 HB |
| 6061 T6 温度 – 抗拉强度极限曲线图 |
 |
| 6061 T6 厚度 – 抗拉强度极限曲线图 |
 |
| 6061 T6 直径 – 抗拉强度极限曲线图 |
 |
6061-T6铝合金是一种通过析出硬化获得中高强度的合金，并广泛应用于工程领域。这种以镁和硅为基础的合金由于其均衡的机械性能而被特别优选。T6状态通过固溶处理和人工时效获得，从而使合金具有较高的抗拉强度和屈服强度。凭借这些性能，它可以安全地应用于结构和半结构应用中。
在耐腐蚀性能方面，6061-T6在许多环境中表现出非常优异的性能，尤其对大气环境具有良好的耐受性。它可以用于海洋环境，但与5083等海洋合金相比，其性能.png)
略低。然而，通过表面处理和涂层可以进一步提高其耐腐蚀性。其可涂覆性很好，通过阳极氧化可以获得既具有保护性又具有美观性的表面。
在强度和加工性能方面, 6061-T6是一种性能均衡的合金。虽然其强度低于7075-T6合金，但其焊接性和加工性要好得多。与2024合金相比，它具有更好的耐腐蚀性和更容易加工的特点。在数控加工、铣削和车削操作中表现良好，并在切削加工过程中被广泛优选。因此，它被广泛应用于汽车、机械和模具行业。
在弯曲和成形性能方面, 在T6状态下其性能有限，但通过适当的工艺可以实现。与T4状态相比，其成形性较低。在振动行为方面，6061合金具有良好的阻尼能.png)
力，因此在结构应用中在振动控制方面具有优势。这一特性在航空航天和运输行业中特别重要。
在焊接性能方面，6061-T6相对于许多铝合金具有明显优势。它可以通过MIG和TIG焊接方法轻松连接。虽然焊接后会出现强度下降，但可以通过适当的热处理部分补偿。其应用领域包括航空航天、汽车、自行车制造、建筑行业、海洋设备以及一般工程应用。与5083、7075和2024 合金相比，6061-T6以其多功能性和均衡性能而突出。
6061 T6 可按以下标准提供：
• 6061 T6 板材; AMS4027, AMSQQ-A-250/11, EN2694, AIR9048.240, UNSA96061, WNR3.3211, ASTM B209
• 6061 T6 薄板; AMS4027, AMSQQ-A-250/11, EN2694, AIR9048.240, UNSA96061, WNR3.3211, ASTM B209
• 6061 T6 冷拉棒; AMS4027, AMSQQ-A-250/11, EN2694, AIR9048.240, UNSA96061, WNR3.3211, ASTM B209
• 6061 T6 冷拉扁条; AMS4027, AMSQQ-A-250/11, EN2694, AIR9048.240, UNSA96061, WNR3.3211, ASTM B209
• 6061 T6 冷拉丝; AMS4027, AMSQQ-A-250/11, EN2694, AIR9048.240, UNSA96061, WNR3.3211, ASTM B209
• 6061 T6 冷拉管; AMS4117, AMSQQ-A-225/8, EN2392, BSL117, UNSA96061, WNR3.3211, ASTM B211
• 6061 T6 挤压棒; AMS4113, AMS4127, AMS4150, AMSQQ-A-200/16（结构型材用）, AMSQQ-A-200/8, ASTM B221
• 6061 T6 挤压扁条; AMS4113, AMS4127, AMS4150, AMSQQ-A-200/16（结构型材用）, AMSQQ-A-200/8, ASTM B221
• 6061 T6 挤压丝; AMS4113, AMS4127, AMS4150, AMSQQ-A-200/16（结构型材用）, AMSQQ-A-200/8, ASTM B221
• 6061 T6 挤压管; AMS4113, AMS4127, AMS4150, AMSQQ-A-200/16（结构型材用）, AMSQQ-A-200/8, ASTM B221
• 6061 T6 挤压锻件; AMS4113, AMS4127, AMS4150, AMSQQ-A-200/16（结构型材用）, AMSQQ-A-200/8, ASTM B221
• 6061 T6 无缝冷拉管; AMS4082, AMS4083（液压管）, WW-T-700/6, MIL-T-7081（液压管）, ASTM B241
6061 T6 选择因素
- 强度: 中等
- 加工性: 良好
- 可焊性: 优秀
- 成形性: 良好
- 耐腐蚀性: 优秀
- 热处理: 是
6061 T6 的典型应用
管道、储罐部件,
耐用消费品结构,
包括摩托艇在内的众多应用。
6061 T6 可生产/供应板材/薄板、圆棒/扁棒以及管材/型材形式。
- 棒材 / 圆棒 / 扁棒
- 板材
- 薄板
- 管材/型材
| 机械性能 | |||
| 厚度 (mm) | 证明力量 (Min.) | 屈服强度 (Min.) | Uzama % |
| Over 0.2 up to & incl. 0.5 | 241 | 290 | %8 |
| Over 0.5 up to & incl. 6.5 | 241 | 290 | %10 |