AMS QQ-A-200/2 / AlCu4SiMg / 2014 / T4510 / T4511
Chemical Properties | % Value |
Silicon (Si) | 0,50 - 1,20 |
Tin (Sn) | 0,0 - 0,15 |
Chromium (Cr) | 0,00 - 0,10 |
Manganese (Mn) | 0,40 - 1,20 |
Magnesium (Mg) | 0,20 - 0,80 |
Copper (Cu) | 3,90 - 5,00 |
Titanium (Ti) | 0,00 - 0,15 |
Iron (Fe) | 0,00 - 0,70 |
Zinc (Zn) | 0,00 - 0,25 |
Aluminium (Al) | Balance |
Physical Properties | Value |
Density | 2800 g/cm³ |
Melting Point | 507 °C |
Thermal Expansion | 22.7 x 10^-6 /K |
Modulus of Elasticity | 73 GPa |
Thermal Conductivity | 150 W/m.K |
Electrical Resistivity | %40 IACS |
Mechanical Properties | Value |
Proof Strength | 280 MPa |
Yield Strength | 430 MPa |
Shear Strength | 260 MPa |
Elongation A50 mm | %17 |
Modulus of Elasticity | 73 GPa |
High strength structural components for aircraft , military vehicles and bridges, weapons manufacture, structural applications.
ALLOY DESIGNATIONS
Aluminium alloy 2014 / 2014A is covered by Standard BS EN 2100 and has similarities to the following standard designations and specifications:
2014 / 2014A, AMS 4029, ISO AlCu4SiMg, 3.1255
DIN AlCuSiMn, UNS A92014, BS L93, DTD 5010
TEMPER TYPES
The most common tempers for 2014 / 2014A aluminium are:
- O - Soft
- T3 - Solution heat treated, cold worked and naturally aged
- T4 - Solution heat treated and naturaly aged to a substantially stable condition
- T6 - Solution heat treated and artificially aged
- T651 - Solution heat treated, stress relieved by stretching then artificially aged