7050

AMS 4050 / AlZn6CuMgZr / 7050 / T7451

Chemical Properties % Value
Silicon (Si)0,00 - 0,12
Chromium (Cr)0,00 - 0,04
Manganese (Mn)0,00 - 0,10
Magnesium (Mg)1,90 - 2,60
Copper (Cu)2,00 - 2,60
Titanium (Ti)0,08 - 0,21
Iron (Fe)0,00 - 0,15
Zinc (Zn)5,70 - 6,70
Aluminium (Al)Balance
Titanium + Zirconium (Ti+Zr)0,08 - 0,15
Physical Properties Value
Density2,80 g/cm³
Thermal Expansion22.1 x 10^-6 /K
Modulus of Elasticity71 GPa
Thermal Conductivity800 j/kg-K
Mechanical Properties Value
Proof Strength450 MPa
Yield Strength550 MPa
Elongation A50 mm%9
Modulus of Elasticity71 GPa
This alloy is used in aircraft structural parts. The alloy has characteristics of high strength coupled with good resistance to exfoliation and stress corrosion cracking. The alloy also has good fracture toughness and fatigue resistance. Aluminum alloy 7050 is the premier choice for aerospace applications requiring the best combination of strength, stress corrosion cracking (SCC) resistance and toughness.

 

ALLOY DESIGNATIONS
Aluminium alloy AMS 4050, 7050 has similarities to the following standard designations and specifications ;

 

Alloy 7050, UNS A97050, ASTM B209

AlZn6CuMgZr, AIR 9048.740

DIN 3.4144, EN3982

 

TEMPER TYPES

7050 is supplied in a wide range of tempers:
  • T73511 - Solution heat-treated, stress-relieved by controlled stretching (permanent set 1% to 3% for extruded rod, bar, shapes and tube, 0.5% to 3% for drawn tube) and then artificially overaged in order to achieve the best stress corrosion resistance. The products receive no further straightening after stretching, except that minor straightening is allowed after stretching to comply with standard tolerances.
  • T7451 - Solution heat-treated, stress-relieved by controlled stretching and then artificially overaged (between T73 and T76). The products receive no further straightening after stretching.
  • T74511 - Solution heat-treated, stress-relieved by controlled stretching and then artificially overaged (between T73 and T76). The pro-ducts receive no further straightening after stretching, except that minor straightening is allowed after stretching to comply with standard tolerances.
  • T76 - Solution heat-treated and then artificially overaged in order to achieve a good exfoliation corrosion resistance.
  • T762 - Solution heat-treated and then artificially overaged in order to achieve a good exfoliation corrosion resistan-ce. Applies to test material heat-treated from annealed or F temper or to products heat-treated from any tem-per by the user.
  • T7651 - Solution heat-treated, stress-relieved by controlled stretching  and then artificially overaged in order to achieve a good exfoliation corrosion resistance. The products recieve no further straightening after stretching.
  • T76511 - Solution heat-treated, stress-relieved by controlled stretching and then artificially overaged in order to achieve a good exfoli-ation corrosion resistance. The products receive no further straightening after stretching, except that minor straightening is allowed after stretching to comply with standard tolerances.
 
 
SUPPLIED FORMS
7050 is supplied in plate, sheet, bar and extrusions.
  • Plate
  • Sheet
  • Round Bar / Bar
  • Tube / Extrusions