5456
AMS QQ-A-200/7 / AlMg5Mn1 / 5456 / H111
| Chemical Properties | % Value |
| Silicon (Si) | 0,00 - 0,25 |
| Chromium (Cr) | 0,05 - 0,20 |
| Manganese (Mn) | 0,50 - 1,00 |
| Magnesium (Mg) | 4,70 - 5,50 |
| Copper (Cu) | 0,00 - 0,10 |
| Titanium (Ti) | 0,00 - 0,20 |
| Iron (Fe) | 0,00 - 0,40 |
| Zinc (Zn) | 0,00 - 0,25 |
| Aluminium (Al) | Balance |
| Physical Properties | Value |
| Density | 2.66 g/cm³ |
| Melting Point | 568 °C |
| Thermal Expansion | 23.9 µm/m.°C |
| Modulus of Elasticity | 69 GPa |
| Thermal Conductivity | 116 W/m.K |
| Electrical Resistivity | 29 % IACS |
| Mechanical Properties | Value |
| Proof Strength | 230 MPa |
| Yield Strength | 320 MPa |
| Shear Strength | 195 MPa |
| Elongation A50 mm | 18% |
| Hardness | 87 HB |
This alloy is primarily used in areas where high strength and better welding parameters are required in a marine vessel or other engineering applications. Alloy 5456 is stocked in tempers H116, H321; to spec ASTM B928. Tempers O, H112, H32; to spec ASTM B209.
ALLOY DESIGNATIONS
5456 H111 has the following standard designations and specifications.
Sheets and plates per; 5456 H111, ISO AlMg5Mn1, ASTM B928, ASTM B209, AMS QQ-A-250/9, UNS A95456, MIL-A-19842C
Cold Drawn Tubes per; 5456 H111, ISO AlMg5Mn1, ASTM B210, UNS A95456, MIL-P-25995
Extruded Round/Flat Bar and Tubes per; 5456 H111, ISO AlMg5Mn1, ASTM B221, UNS A95456, MIL-A-21170A, AMS QQ-A-200/7
Choosing Factors for 5456 H111
- Strength: Moderate
- Machining: Weak
- Weldability: Very good
- Formability: Poor
- Corrosion Resistance: Excellent
- Heat Treating: None
Some Well-Known Applications for 5456 H111
In high-strength welded structures,
In overhead cranes,
It is also used in automotive industry.
SUPPLIED FORMS
5456 H111 is produced/supplied in the sheet, tube/profile, round/flat bar forms.
- Sheet
- Round/Flat Bar
- Tube/Profile
- Plate