6061
EN AW / AlMg1SiCu / 6061 / T42
| 化学性质 | % 值 |
| Silicon (Si) | 0,40 - 0,80 |
| Chromium (Cr) | 0,04 - 0,35 |
| Manganese (Mn) | 0,00 - 0,15 |
| Magnesium (Mg) | 0,80 - 1,20 |
| Copper (Cu) | 0,15 - 0,40 |
| Titanium (Ti) | 0,00 - 0,15 |
| Iron (Fe) | 0,00 - 0,70 |
| Zinc (Zn) | 0,00 - 0,25 |
| Aluminium (Al) | Balance |
| 物理特性 | 值 |
| Density | 2.70 g/cm³ |
| Melting Point | 582 °C |
| Thermal Expansion | 23.4 µm/m.°C |
| Modulus of Elasticity | 69 GPa |
| Thermal Conductivity | 170 W/m.K |
| Electrical Resistivity | 43% IACS |
| 机械性能 | 值 |
| Proof Strength | 110 MPa |
| Yield Strength | 230 MPa |
| Shear Strength | 140 MPa |
| Elongation A50 mm | 18% |
| Hardness | 57 HB |
6061 T42 aluminum exhibits mid strength and is widely used in aerospace applications.
ALLOY DESIGNATIONS
6061 T42 has the following standard designations and specifications.
As Plate/Sheet; 6061 T42, UNS A96061, WNR 3.3211, ISO AlMg1SiCu, ASTM B209
Choosing Factors for 6061 T42
- Strength: Mediocre
- Machining: Good
- Weldability: Excellent
- Formability: Normal
- Corrosion Resistance: Exquisite
- Heat Treating: Yes
Some Well-Known Applications for 6061 T42
Cargo doors of airplanes and helicopters,
In architectural applications,
In the machinery industry, it is used as machine equipment and fasteners.
SUPPLIED FORMS
6061 T42 is produced/supplied in sheet and plate forms.
- Sheet
- Plate
交货:
| 机械性能 | |||
| 厚度 (mm) | 证明力量 (Min.) | 屈服强度 (Min.) | Uzama % |
| Over 0.4 up to & incl. 1.5 | 241 | 262 | %8 |
| Over 1.5 up to & incl. 3.0 | 241 | 262 | %14 |
| Over 3.0 up to & incl. 6.0 | 241 | 262 | %16 |
| Over 6.0 up to & incl. 12.0 | 241 | 262 | %18 |