AMS QQ-A-200/2 / AlCu4SiMg / 2014 / T6
| 化学性质 | % 值 |
| Silicon (Si) | 0,50 - 0,90 |
| Chromium (Cr) | 0,00 - 0,10 |
| Manganese (Mn) | 0,40 - 1,20 |
| Magnesium (Mg) | 0,20 - 0,80 |
| Copper (Cu) | 3,90 - 5,00 |
| Titanium (Ti) | 0,00 - 0,15 |
| Iron (Fe) | 0,00 - 0,50 |
| Zinc (Zn) | 0,00 - 0,25 |
| Nickel (Ni) | 0,00 - 0,10 |
| Aluminium (Al) | Balance |
| 物理特性 | 值 |
| Density | 2.80 g/cm³ |
| Melting Point | 505 °C |
| Thermal Expansion | 22.8 µm/m°C |
| Modulus of Elasticity | 72 GPa |
| Thermal Conductivity | 160 W/m.K |
| Electrical Resistivity | %40 IACS |
| 机械性能 | 值 |
| Proof Strength | 424 MPa |
| Yield Strength | 493 MPa |
| Shear Strength | 290 MPa |
| Elongation A50 mm | 7% |
| Hardness | 140 HB |
2014 T6 aluminum exhibits high strength and is widely used in aerospace applications.
ALLOY DESIGNATIONS
2014 T6 has the following standard designations and specifications.
As Sheet/Plate; 2014 T6, ASTM B209, ISO AlCu4SiMg, UNS A92014, AIR 9048.040
As Extruded Round/Flat Bar, Tube; 2014 T6, AMS QQ-A-200/2, ASTM B221, UNS A92014, AMS 4153
As Cold Drawn Round/Flat Bar,Tube :2014 T6, AMS 4121, AMS QQ-A-225/4 ASTM B211, UNS A92014, ASTM B928
Choosing Factors for 2014 T6
- Strength: Very good
- Machining: Very good
- Weldability: Poor
- Formability: Okay
- Corrosion Resistance: Weak
- Heat Treating: Yes
Some Well-Known Applications for 2014 T6
As a high-resistant material in aerospace,
As equipment material in the defense and military industry,
Automotive industry is also one of the areas where it is used.
SUPPLIED FORMS
2014 T6 is produced/supplied in plate/sheet, round/flat bar and tube/profile forms.
- Plate/Sheet
- Rod / Round Bar / Flat Bar
- Tube/Profile
交货:
| 机械性能 | |||
| 厚度 (mm) | 证明力量 (Min.) | 屈服强度 (Min.) | Uzama % |
| Over 25 up to & incl. 75 | 415 MPa | 460 MPa | %7 |
| Over 150 up to & incl. 200 | 350 MPa | 430 MPa | %6 |
| Over 200 up to & incl. 250 | 320 MPa | 420 MPa | %5 |