5086
EN AW / AlMg4 / 5086 / H32
| Chemical Properties | % Value |
| Silicon (Si) | 0,00 - 0,40 |
| Chromium (Cr) | 0,05 - 0,25 |
| Magnesium (Mg) | 3,50 - 4,50 |
| Manganese (Mn) | 0,20 - 0,70 |
| Titanium (Ti) | 0,00 - 0,15 / - |
| Iron (Fe) | 0,00 - 0,50 |
| Zinc (Zn) | 0,00 - 0,25 |
| Aluminium (Al) | Balance |
| Physical Properties | Value |
| Density | 2.66 g/cm³ |
| Melting Point | 585 °C |
| Thermal Expansion | 23.8 µm/m.°C |
| Modulus of Elasticity | 71 GPa |
| Thermal Conductivity | 125 W/m.K |
| Electrical Resistivity | %31 IACS |
| Mechanical Properties | Value |
| Proof Strength | 220 MPa |
| Yield Strength | 300 MPa |
| Shear Strength | 175 MPa |
| Elongation A50 mm | 13% |
| Hardness | 78 HB |
5086 aluminum exhibits higher strength than 5052 and has excellent corrosion resistance in marine and salt water environments. It is easy to form, stamp and weld.
ALLOY DESIGNATIONS
5086 H32 has the following standard designations and specifications.
As Plate/Sheet; 5086 H32, AMS QQ-A-250/7, ASTM B209, ISO AlMg4, DIN AlMg4Mn UNS A95086, ASTM B632, ASTM B928, AMS QQ-A-250/19, WNR 3.3545
As Cold Drawn 5086 H32, ASTM B211, UNS A95086, ASTM B928, ASTM B210, WNR 3.3545, DIN AlMg4Mn
Choosing Factors for 5086 H32
- Strength: Good
- Machining: Fairly good
- Weldability: Good
- Formability: Very Good
- Corrosion Resistance: Great
- Heat Treating: Yes
Some Well-Known Applications for 5086 H32
Especially in maritime and marine and boat materials.
As a structural component of missiles,
It is also preferred in radio towers, armor plating and tank components.
SUPPLIED FORMS
5086 H32 is produced/supplied in plate/sheet, round/flat bar and tube/profile forms.
- Plate
- Sheet
- Rod / Round Bar / Flat Bar
- Tube/Profile