6013
ASTM B209 / AlMg1Si0.8CuMn / 6013 / T651
| 化学性质 | % 值 |
| Silicon (Si) | 0,60 - 1,00 |
| Chromium (Cr) | 0,00 - 0,10 |
| Manganese (Mn) | 0,20 - 0,80 |
| Magnesium (Mg) | 0,80 - 1,20 |
| Copper (Cu) | 0,60 - 1,10 |
| Titanium (Ti) | 0,00 - 0,10 |
| Iron (Fe) | 0,00 - 0,50 |
| Zinc (Zn) | 0,00 - 0,25 |
| Aluminium (Al) | Balance |
| 物理特性 | 值 |
| Density | 2,71 g/cm³ |
| Melting Point | 579 °C |
| Thermal Expansion | 21.7 µm/m.°C |
| Modulus of Elasticity | 71 GPa |
| Thermal Conductivity | 164 W/m.K |
| Electrical Resistivity | %38 IACS |
| 机械性能 | 值 |
| Proof Strength | 350 MPa |
| Yield Strength | 410 MPa |
| Shear Strength | 240 MPa |
| Elongation A50 mm | 4% |
| Hardness | 130 HB |
6013 T651 aluminum exhibits mid strength and is widely used in aerospace applications.
ALLOY DESIGNATIONS
6013 T651 has the following standard designations and specifications.
Plates per; 6013 T651, AMS 4347, UNS A96013, ASTM B209, ISO AlMg1Si0.8CuMn
Extruded Round/Flat Bar, Wire,Tubes per: 6013 T651, UNS A96013, ASTM B221, ISO AlMg1Si0.8CuMn
Choosing Factors for 6013 T651
- Strength: High
- Machining: Mid-high
- Weldability: Average
- Formability: Satisfactory
- Corrosion Resistance: Very good
- Heat Treating: Yes
Some Well-Known Applications for 6013 T651
In valve and machine parts,
In car hoods and bumpers,
It is also used in the defense industry..
.
SUPPLIED FORMS
6013 T651 is produced/supplied in plate , round/flat bar and tube/profile forms.
- Rod / Round Bar / Flat Bar
- Plate
- Tube/Profile