EN AW / AlMg3.5 / 5154 / H22
| Chemical Properties | % Value |
| Silicon (Si) | 0,00 - 0,25 |
| Chromium (Cr) | 0,15 - 0,35 |
| Manganese (Mn) | 0,00 - 0,10 |
| Magnesium (Mg) | 3,10 - 3,90 |
| Copper (Cu) | 0,00 - 0,10 |
| Titanium (Ti) | 0,00 - 0,20 |
| Iron (Fe) | 0,00 - 0,40 |
| Zinc (Zn) | 0,00 - 0,20 |
| Aluminium (Al) | Balance |
| Physical Properties | Value |
| Density | 2,66 g/cm³ |
| Melting Point | 593 °C |
| Thermal Expansion | 23.9 µm/m.°C |
| Modulus of Elasticity | 69 GPa |
| Thermal Conductivity | 130 W/m.K |
| Electrical Resistivity | 32% IACS |
| Mechanical Properties | Value |
| Proof Strength | 200 MPa |
| Yield Strength | 270 MPa |
| Shear Strength | 160 MPa |
| Elongation A50 mm | 14% |
| Hardness | 67 HB |
Aluminium Alloy 5154 primary constituent is magnesium which gives this non heat treatable alloy its moderate strength. Alloy 5154 combines its strength with excellent formabiltiy and corrosion resistance and is regularly used in wire form but is now becoming popular for use with cold heading applications, specifically in solid, semi-tubular and tubular rivets. Alloy 5154 is an all purpose alloy that meets a broad range of needs.
ALLOY DESIGNATIONS
5154 H22 has the following standard designations and specifications.
Sheets and plates per; 5154 H22, ISO AlMg3.5, DIN AlMg3, WNR 3.3535, UNS A95154, ASTM B209
Choosing Factors for 5154 H22
- Strength: Moderate
- Machining: Decent
- Weldability: Okay
- Formability: Very good
- Corrosion Resistance: Excellent
- Heat Treating: None
Some Well-Known Applications for 5154 H22
In machines in packing lines,
In architectural façades,
It is also used in welded structures and storage tanks
SUPPLIED FORMS
5154 H22 is produced/supplied in the plate and sheet forms.
- Sheet
- Plate
DELIVERY:
Calculador de Peso