BS N41 / AlMg1 / 5005 / H18
| 化学性质 | % 值 |
| Silicon (Si) | 0,00 - 0,30 |
| Chromium (Cr) | 0,00 - 0,10 |
| Manganese (Mn) | 0,00 - 0,20 |
| Magnesium (Mg) | 0,50 - 1,10 |
| Copper (Cu) | 0,00 - 0,20 |
| Iron (Fe) | 0,00 - 0,70 |
| Zinc (Zn) | 0,00 - 0,25 |
| Aluminium (Al) | Balance |
| 物理特性 | 值 |
| Density | 2.68 g/cm³ |
| Melting Point | 632 °C |
| Thermal Expansion | 23.8 µm/m.°C |
| Modulus of Elasticity | 68 GPa |
| Thermal Conductivity | 200 W/m.K |
| Electrical Resistivity | 52% IACS |
| 机械性能 | 值 |
| Proof Strength | 193 MPa |
| Yield Strength | 210 MPa |
| Shear Strength | 110 MPa |
| Elongation A50 mm | 3% |
| Hardness | 58 HB |
5005 H18 has excellent finishing qualities and anodized coatings. Weldability is very good and 5005 H18 has good resistance to corrosion, especially in anodised. Alloy 5005 H18 sheets' typical uses are also included below.
ALLOY DESIGNATIONS
5005 H18 has the following standard designations and specifications.
Sheets per; 5005 H18, ISO AlMg1, DIN AlMg1, WNR 3.3315, UNS A95005, ASTM B209, BS N41
Cold Drawn Round/Flat Bar per; 5005 H18, ISO AlMg1, DIN AlMg1, WNR 3.3315, UNS A95005, ASTM B211
Cold Drawn Tubes per; 5005 H18, ISO AlMg1, DIN AlMg1, WNR 3.3315, UNS A95005, ASTM B210
Choosing Factors for 5005 H18
- Strength: Mediocre
- Machining: Poor
- Weldability: Very good
- Formability: Good
- Corrosion Resistance: Excellent
- Heat Treating: None
Some Well-Known Applications for 5005 H18
In architectural applications,
In construction of high-strength foils,
It is also used in clad-roofing.
SUPPLIED FORMS
5005 H18 is produced/supplied in the sheet, tube/profile, round/flat bar forms.