WNR 3.3315 / AlMg1 / 5005 / H14
| Chemical Properties | % Value |
| Silicon (Si) | 0,00 - 0,30 |
| Chromium (Cr) | 0,00 - 0,10 |
| Manganese (Mn) | 0,00 - 0,20 |
| Magnesium (Mg) | 0,50 - 1,10 |
| Copper (Cu) | 0,00 - 0,20 |
| Iron (Fe) | 0,00 - 0,70 |
| Zinc (Zn) | 0,00 - 0,25 |
| Aluminium (Al) | Balance |
| Physical Properties | Value |
| Density | 2.68 g/cm³ |
| Melting Point | 607 °C |
| Thermal Expansion | 23.8 µm/m.°C |
| Modulus of Elasticity | 68 GPa |
| Thermal Conductivity | 200 W/m.K |
| Electrical Resistivity | %52 IACS |
| Mechanical Properties | Value |
| Proof Strength | 140 MPa |
| Yield Strength | 160 MPa |
| Shear Strength | 96 MPa |
| Elongation A50 mm | 5% |
| Hardness | 48 HB |
5005 H14 has excellent finishing qualities and anodized coatings. Weldability is very good and 5005 H14 has good resistance to corrosion, especially in anodised. Alloy 5005 H14 sheet's typical uses are also included below.
ALLOY DESIGNATIONS
5005 H14 has the following standard designations and specifications.
Sheets per; 5005 H14, ISO AlMg1, DIN AlMg1, WNR 3.3315, UNS A95005, ASTM B209, BS N41
Cold Drawn Round/Flat Bar per; 5005 H14, ISO AlMg1, DIN AlMg1, WNR 3.3315, UNS A95005, ASTM B211
Cold Drawn Tubes per; 5005 H14, ISO AlMg1, DIN AlMg1, WNR 3.3315, UNS A95005, ASTM B210
Choosing Factors for 5005 H14
- Strength: Moderate
- Machining: Fair
- Weldability: Excellent
- Formability: Good
- Corrosion Resistance: Excellent
- Heat Treating: None
Some Well-Known Applications for 5005 H14
It is used in furniture making,
In anodized parts,
It is also used in machine and engine componentry.
SUPPLIED FORMS
5005 H14 is produced/supplied in the sheet, tube/profile, round/flat bar forms.
- Sheet
- Round/Flat Bar
- Tube/Profile
DELIVERY:
Weight Calculator