2033
ASME SB211 / AW-2033 / 2033 / T3
| Chemical Properties | % Value |
| Silicon (Si) | 0,10 - 1,20 |
| Chromium (Cr) | 0,00 - 0,15 |
| Manganese (Mn) | 0,40 - 1,00 |
| Magnesium (Mg) | 0,20 - 0,60 |
| Copper (Cu) | 2,20 - 2,70 |
| Titanium (Ti) | 0,00 - 0,10 |
| Iron (Fe) | 0,00 - 0,50 |
| Zinc (Zn) | 0,00 - 0,50 |
| Aluminium (Al) | Balance |
| Nickel (Ni) | 0,00 - 0,15 |
| Physical Properties | Value |
| Density | 2.77 g/cm³ |
| Melting Point | 502 °C |
| Thermal Expansion | 22,9 µm/m.°C |
| Modulus of Elasticity | 70 GPa |
| Thermal Conductivity | 151 W/m.K |
| Electrical Resistivity | 0,046 Ωmm² /m |
| Mechanical Properties | Value |
| Proof Strength | 230 MPa |
| Yield Strength | 355 MPa |
| Shear Strength | 283 MPa |
| Elongation A50 mm | 8% |
| Hardness | 100 HB |
A medium to high strength alloy with, dependent upon temper, minimum Proof Stress up to 57 ksi / 390 Mpa and minimum Tensile Strength up to 66 ksi / 455 MPa
ALLOY DESIGNATIONS
Aluminium alloy 2033 T3 has similarities to the following standard designations and specifications:
Cold Drawn Round/Flat Bars per; 2033 T3, 2000/53/EU (ELV) - 2018/740/EU (RoHS II), UNS A92033, ASTM B211
Cold Drawn Tubes per; 2033 T3, 2000/53/EU (ELV) - 2018/740/EU (RoHS II), UNS A92033, ASTM B210
Choosing Factors for 2033 T3
- Strength: Very good
- Machining: Very good
- Weldability: Moderate
- Formability: Poor
- Corrosion Resistance: Low
- Heat Treating: Yes
Some Well-Known Applications for 2033 T3
In the automotive industry,
In precision machining,
It is also used in manufacturing of nuts and bolts.
SUPPLIED FORMS
2033 T3 is supplied in round/flat bar and tube/ profile forms.
- Flat/round bar
- Tube/profile
DELIVERY:
| Mechanical Properties | |||
| Thickness (mm) | Proof Strength (Min.) | Yield Strength (Min.) | Elongation A50 mm % |
| Over 2,5 up to & incl. 30,00 mm | 240 MPa | 370 MPa | 7% |
| Over 30 up to & incl. 80,00 mm | 220 MPa | 340 MPa | 7% |