2017A
ASTM B221 / AlCu4MgSi(A) / 2017A / T4510/T4511
| 化学性质 | % 值 |
| Silicon (Si) | 0,20 - 0,80 |
| Chromium (Cr) | 0,00 - 0,10 |
| Manganese (Mn) | 0,40 - 1,0 |
| Magnesium (Mg) | 0,40 - 1,00 |
| Copper (Cu) | 3,50 - 4,50 |
| Titanium (Ti) | 0,00 - 0,25 |
| Iron (Fe) | 0,00 - 0,70 |
| Zinc (Zn) | 0,00 - 0,25 |
| Aluminium (Al) | Balance |
| 物理特性 | 值 |
| Density | 2.79 g/cm³ |
| Melting Point | 510 °C |
| Thermal Expansion | 23.6 µm/m.°C |
| Modulus of Elasticity | 72 GPa |
| Thermal Conductivity | 150 W/m.K |
| Electrical Resistivity | 34 % IACS |
| 机械性能 | 值 |
| Proof Strength | 270 MPa |
| Yield Strength | 410 MPa |
| Shear Strength | 240 MPa |
| Elongation A50 mm | 8% |
| Hardness | 105 HB |
2017A T4510/T4511 aluminum exhibits high strength and is widely used in aerospace applications.
ALLOY DESIGNATIONS
2017A T4510/T4511 has the following standard designations and specifications.
As Extruded Round/Flat Bar, Profile: 2017A T4510/T4511, AMS QQ-A-225/5, ASTM B221, UNS A92017A, WNR 3.1325, DIN AlCuMg1, ASTM B565, ASTM B316, ISO AlCu4MgSi (A)
Choosing Factors for 2017A T4510/ T4511
- Strength: Excellent
- Machining: Great
- Weldability: Mediocre
- Formability: Okay
- Corrosion Resistance: Average
- Heat Treating: Yes
Some Well-Known Applications for 2017A T4510/4511
As a high-strength structural material in various sectors,
In the automotive and aerospace industry,
It is also found in the structure of measuring tools and rivet nails.
SUPPLIED FORMS
2017A T4510/T4511 is produced/supplied in round/flat bar and tube/profile forms.
- Rod / Round Bar / Flat Bar
- Tube/Profile
交货:
| 机械性能 | |||
| 厚度 (mm) | 证明力量 (Min.) | 屈服强度 (Min.) | Uzama % |
| Over 25 up to & incl. 75 | 270 MPa | 400 MPa | %10 |
| Over 75 up to & incl. 150 | 260 MPa | 390 MPa | %9 |
| Over 150 up to & incl. 200 | 240 MPa | 370 MPa | %8 |
| Over 200 up to & incl. 250 | 220 MPa | 360 MPa | %7 |