ASTM B210 / AlCu4SiMg / 2014A / T351
| 化学性质 | % 值 |
| Silicon (Si) | 0,50 - 0,90 |
| Chromium (Cr) | 0,00 - 0,10 |
| Manganese (Mn) | 0,40 - 1,20 |
| Magnesium (Mg) | 0,20 - 0,80 |
| Copper (Cu) | 3,90 - 5,00 |
| Titanium (Ti) | 0,00 - 0,20 |
| Iron (Fe) | 0,00 - 0,50 |
| Zinc (Zn) | 0,00 - 0,25 |
| Aluminium (Al) | Balance |
| Titanium + Zirconium (Ti+Zr) | 0,00 - 0,20 |
| 物理特性 | 值 |
| Density | 2.80 g/cm³ |
| Melting Point | 510 °C |
| Thermal Expansion | 22.8 µm/m.°C |
| Modulus of Elasticity | 73 GPa |
| Thermal Conductivity | 155 W/m.K |
| Electrical Resistivity | 40% IACS |
| 机械性能 | 值 |
| Proof Strength | 330 MPa |
| Yield Strength | 430 MPa |
| Shear Strength | 250 MPa |
| Elongation A50 mm | 6.7 % |
| Hardness | 120 HB |
2014A T351 aluminum exhibits high strength and is widely used in aerospace applications.
ALLOY DESIGNATIONS
2014A T351 has the following standard designations and specifications.
Cold Drawn Round/Flat Bars per : 2014A T351, ISO AlCu4SiMg, MIL-A-A21180, ASTM B211, UNS A92014, WNR 3.1255
Cold Drawn Tubes per; 2014A T351, ISO AlCu4SiMg, MIL-A-21180, ASTM B210, UNS A92014, WNR 3.1255
Choosing Factors for 2014A T351
- Strength: Exquisite
- Machining: Great
- Weldability: Bad
- Formability: Good
- Corrosion Resistance: Poor
- Heat Treating: Yes
Some Well-Known Applications for 2014A T351
In the automotive industry and defense industry,
In military vehicles and hydraulic applications,
It is also used in the automotive industry and as aircraft construction material.
SUPPLIED FORMS
2014A T351 is produced/supplied in plate/sheet, round/flat bar and tube/profile forms.
- Plate/Sheet
- Rod / Round Bar / Flat Bar
- Tube/Profile
交货:
| 机械性能 | |||
| 厚度 (mm) | 证明力量 (Min.) | 屈服强度 (Min.) | Uzama % |
| Over 0.4 up to & incl. 0.8 | 370 MPa | 430 MPa | %6 |
| Over 0.8 up to & incl. 1.6 | 380 MPa | 440 MPa | %7 |
| Over 1,6 up to & incl. 6,0 | 390 MPa | 440 MPa | %7 |