5754
CR 1.1.0.18 / AlMg3 / 5754 / H111
| 化学性质 | % 值 |
| Silicon (Si) | 0,00 - 0,25 |
| Chromium (Cr) | 0,05 - 0,20 |
| Manganese (Mn) | 0,00 - 0,50 |
| Magnesium (Mg) | 2,60 - 3,60 |
| Copper (Cu) | 0,00 - 0,10 |
| Titanium (Ti) | 0,00 - 0,20 |
| Iron (Fe) | 0,00 - 0,40 |
| Zinc (Zn) | 0,00 - 0,25 |
| Aluminium (Al) | Balance |
| 物理特性 | 值 |
| Density | 2,67 g/cm³ |
| Melting Point | 598 °C |
| Thermal Expansion | 23.9 µm/m.°C |
| Modulus of Elasticity | 69 GPa |
| Thermal Conductivity | 120 W/m.K |
| Electrical Resistivity | 33% IACS |
| 机械性能 | 值 |
| Proof Strength | 90 MPa |
| Yield Strength | 210 MPa |
| Shear Strength | 130 MPa |
| Elongation A50 mm | %13 |
| Hardness | 52 HB |
5754 H111 exhibits mid strength and is applicable for general industry uses.
ALLOY DESIGNATIONS
5754 H111 has the following standard designations and specifications.
Sheets and Plates per; 5754 H111, ASTM B209, UNS A95754, WNR 3.3535, UNI AlMg3.5, UNE L-3390, AFNOR A-G3M, CR 1.1.0.18
Extruded Round/Flat Bars and Tubes per; 5754 H111, ASTM B221, UNS A95754, WNR 3.3535, UNI AlMg3.5, UNE L-3390, AFNOR A-G3M, CR 1.1.0.18
Choosing Factors for 5754 H111
- Strength: Good
- Machining: Poor
- Weldability: Very good
- Formability: Medium
- Corrosion Resistance: Good
- Heat Treating: No
Some Well-Known Applications for 5754 H111
Boilermaking industry,
As tread plates,
In welded chemical structures.
SUPPLIED FORMS
5754 H111 is produced/supplied in plate/sheet, round/flat bar and tube/profile forms.
- Plate
- Sheet
- Rod / Round Bar / Flat Bar
- Tube/Profile
交货:
| 机械性能 | |||
| 厚度 (mm) | 证明力量 (Min.) | 屈服强度 (Min.) | Uzama % |
| Over 0.2 up to & incl. 0.5 | ≥ 80 MPa | 190–240 MPa | ≥ 12 |
| Over 0.5 up to & incl. 1.5 | ≥ 80 MPa | 190–240 MPa | ≥ 14 |
| Over 1.5 up to & incl. 3.0 mm | ≥ 80 MPa | 190–240 MPa | ≥ 14 |
| Over 3.0 up to & incl. 12.5 mm | ≥ 80 MPa | 190–240 MPa | ≥ 18 |
| Over 12.5 up to & incl. 100 mm | ≥ 80 MPa | 190–240 MPa | ≥ 19 |