ASTM B210 / Al99.0 / 1200 / O
| 化学性质 | % 值 |
| Silicon (Si) | 0,00 - 0,10 |
| Manganese (Mn) | 0,00 - 0,05 |
| Copper (Cu) | 0,00 - 0,05 |
| Titanium (Ti) | 0,00 - 0,05 |
| Iron (Fe) | 0,00 - 1,00 |
| Zinc (Zn) | 0,00 - 0,10 |
| Aluminium (Al) | Balance |
| 物理特性 | 值 |
| Density | 2,70 g/cm³ |
| Melting Point | 654°C |
| Thermal Expansion | 23.4 µm/m.°C |
| Modulus of Elasticity | 70 GPa |
| Thermal Conductivity | 230 W/m.K |
| Electrical Resistivity | %59 IACS |
| 机械性能 | 值 |
| Proof Strength | 29 MPa |
| Yield Strength | 88 MPa |
| Shear Strength | 57 MPa |
| Elongation A50 mm | 28% |
| Hardness | 23 HB |
Very good atmospheric corrosion resistance and workability. High thermal conductivity and reflectivity but lower than for 1050A. Very good weldability. Slightly higher strength than 1050A but low in general.
ALLOY DESIGNATIONS
1200 O has the following standard designations and specifications.
Sheets per; 1200 O, ASTM B209, BS 6 L17, UNS A91200, BS 1C, ISO Al99.0, DIN Al99, WNR 3.0205
Cold Drawn Round/Flat Bar, Wires per; 1200 O, ASTM B211, BS 1C, UNS A91200, ISO Al99.0, DIN Al99, WNR 3.0205
Cold Drawn Tubes per; 1200 O, ASTM B210, BS L116, BS 4L54 (Hydraulic Tube) UNS A91200, BS 1C, ISO Al99.0, DIN Al99, WNR 3.0205
Choosing Factors for 1200 O
- Strength: Average
- Machining: Poor
- Weldability: Excellent
- Formability: Very good
- Corrosion Resistance: Perfect
- Heat Treating: Yes
Some Well-Known Applications for 1200 O
In home furniture and lighting parts,
In bottle production,
Also used in kitchenware.
SUPPLIED FORMS
1200 O is produced/supplied in the sheet, round/flat bar and tube/profile form.
- Sheets
- Round/Flat Bar
- Tube/Profile
交货:
| 机械性能 | |||
| 厚度 (mm) | 证明力量 (Min.) | 屈服强度 (Min.) | Uzama % |
| Min %20 | |||
计算 重量计算