2014A
Cold Drawn/Finished (CF) / AlCu4SiMg (Soğuk Çekim) / 2014A / T651
| 化学性质 | % 值 |
| Silicon (Si) | 0,50 - 0,90 |
| Chromium (Cr) | 0,00 - 0,10 |
| Manganese (Mn) | 0,40 - 1,20 |
| Magnesium (Mg) | 0,20 - 0,80 |
| Copper (Cu) | 3,90 - 5,00 |
| Titanium (Ti) | 0,00 - 0,15 |
| Iron (Fe) | 0,00 - 0,50 |
| Zinc (Zn) | 0,00 - 0,25 |
| Nickel (Ni) | 0,00 - 0,10 |
| Aluminium (Al) | Balance |
| 物理特性 | 值 |
| Density | 2.80 g/cm³ |
| Melting Point | 507 °C |
| Thermal Expansion | 22.5 µm/m.°C |
| Modulus of Elasticity | 73 GPa |
| Thermal Conductivity | 155 W/m.K |
| Electrical Resistivity | 37% IACS |
| 机械性能 | 值 |
| Proof Strength | 414 MPa |
| Yield Strength | 510 MPa |
| Shear Strength | 290 MPa |
| Elongation A50 mm | 7% |
| Hardness | 135 HB |
2014A T651 aluminum exhibits which is used for military, aerospace and structural applications, also exhibits high strength.
ALLOY DESIGNATIONS
2014A T651 has the following standard designations and specifications.
As Sheet/Plate; 2014A T651, ASTM B209, ISO AlCu4SiMg, UNS A9201, BS 2 L93, WNR 3.1255
As Cold Drawn Round/Flat Bar, Tube : 2014A T651, ASTM B211, UNS A92014, ASTM B928, WNR 3.1255
Choosing Factors for 2014A T651
- Strength: Perfect
- Machining: Very good
- Weldability: Weak
- Formability: Okay
- Corrosion Resistance: Weak
- Heat Treating: Yes
Some Well-Known Applications for 2014A T651
Heat exchangers, cooling towers,
In military vehicle construction and weapons production,
It is generally used in the aerospace and automotive industries.
SUPPLIED FORMS
2014A T651 is produced/supplied in plate/sheet, round/flat bar and tube/profile forms.
- Plate/Sheet
- Rod / Round Bar / Flat Bar
- Tube/Profile
交货:
| 机械性能 | |||
| 厚度 (mm) | 证明力量 (Min.) | 屈服强度 (Min.) | Uzama % |
| Up to & incl 2.5 | 370 MPa | 415 MPa | %6 |
| Over 2.5 up to and incl. 10 | 385 MPa | 435 MPa | %6 |
| Over 10 up to and incl. 25 | 415 MPa | 460 MPa | %7 |
| Over 75 up to and incl. 100 | 435 MPa | 480 MPa | %7 |
| Over 100 up to and incl. 150 | 420 MPa | 465 MPa | %7 |
| Over 150 up to and incl. 200 | 390 MPa | 435 MPa | %7 |