6005A
ASTM B221 / AlSiMg(A) / 6005A / T6
| Chemical Properties | % Value |
| Silicon (Si) | 0,50 - 0,90 |
| Chromium (Cr) | 0,00 - 0,30 |
| Manganese (Mn) | 0,00 - 0,50 |
| Magnesium (Mg) | 0,40 - 0,70 |
| Copper (Cu) | 0,00 - 0,30 |
| Titanium (Ti) | 0,00 - 0,10 |
| Iron (Fe) | 0,00 - 0,35 |
| Zinc (Zn) | 0,00 - 0,20 |
| Aluminium (Al) | Balance |
| Physical Properties | Value |
| Density | 2.63 g/cm³ |
| Melting Point | 582 °C |
| Thermal Expansion | 23.4 µm/m.°C |
| Modulus of Elasticity | 69 GPa |
| Thermal Conductivity | 189 W/m.K |
| Electrical Resistivity | %49 IACS |
| Mechanical Properties | Value |
| Proof Strength | 230 MPa |
| Yield Strength | 280 MPa |
| Shear Strength | 170 MPa |
| Elongation A50 mm | 9% |
| Hardness | 95 HB |
6005A alloy, which exhibits mechanical values in between that of 6061 and 6082 is welded best using arc welding and has superior corrosion resistance and good anodizing.
ALLOY DESIGNATIONS
6005A T6 has the following standard designations and specifications.
Cold Drawn Round/Flat Bars per; 6005A T6, ISO AlSiMg(A), UNI 9006/6, DIN AlMgSi0.7, AFNOR A-GS0.5, UNE L-3454, WNR 3.3210, ASTM B211
Choosing Factors for 6005A T6
- Strength: Moderate
- Machining: Fair
- Weldability: Very good (Arc welding is the best choice)
- Formability: Moderate
- Corrosion Resistance: Good
- Heat Treating: Yes
Some Well-Known Applications for 6005A T6
In tubings of furnitures,
In railway transport industry and buses,
It is also used in ladder construction.
SUPPLIED FORMS
6005A T6 is produced/supplied in plate/sheet round/flat bar and tube/profile forms.
- Rod / Round Bar / Flat Bar
- Tube/Profile
DELIVERY:
| Mechanical Properties | |||
| Thickness (mm) | Proof Strength (Min.) | Yield Strength (Min.) | Elongation A50 mm % |
| Over 0.2 up to & incl. 0.5 | 241 | 290 | %8 |
| Over 0.5 up to & incl. 6.5 | 241 | 290 | %10 |