Cold Drawn/Finished (CF) / AlCu4PbMgMn (Soğuk Çekim) / 2007 / T351
| Chemical Properties | % Value |
| Silicon (Si) | 0,80 Max |
| Copper (Cu) | 3,30 - 4,60 |
| Lead (Pb) | 0,80 - 1,50 |
| Iron (Fe) | 0,80 Max |
| Zinc (Zn) | 0,00 - 0,80 |
| Nickel (Ni) | 0,00 - 0,20 |
| Aluminium (Al) | Balance |
| Magnesium (Mg) | 0,40 - 1,80 |
| Manganese (Mn) | 0,50 - 1,00 |
| Physical Properties | Value |
| Density | 2.82 g/cm³ |
| Melting Point | 510 °C |
| Thermal Expansion | 23.0 µm/m.°C |
| Modulus of Elasticity | 73 GPa |
| Thermal Conductivity | 130 W/m.K |
| Electrical Resistivity | %47 IACS |
| Mechanical Properties | Value |
| Proof Strength | 270 MPa |
| Yield Strength | 410 MPa |
| Shear Strength | 240 MPa |
| Elongation A50 mm | 6% |
| Hardness | 105 HB |
An aluminum-copper alloy that typically contains between 4.0 and 5.0 % of copper, it is suitable for producing machine parts, bolts and rivets. It resembles very much to 2011 alloy, while being a bit more harder.
ALLOY DESIGNATIONS
2007 T351 has the following standard designations and specifications.
Cold Drawn Round/Flat Bars per; 2007 T351, WNR 3.1645, DIN AlCuMgPb, AFNOR A-U4Pb, UNI 9002/8, UNE L-3121, UNS A92007, ISO AlCu4PbMgMn
Cold Drawn Tubes per; 2007 T351, WNR 3.1645, DIN AlCuMgPb, AFNOR A-U4Pb, UNI 9002/8, UNE L-3121, UNS A92007, ISO AlCu4PbMgMn
Choosing Factors for 2007 T351
- Strength: High
- Machining: Good
- Weldability: Weak
- Formability: Poor
- Corrosion Resistance: Poor
- Heat Treating: Yes
Some Well-Known Applications for 2007 T351
Milled and turned parts,
As components of fans,
It is also used in threaded rods.
SUPPLIED FORMS
2007 T351 is produced/supplied in round/flat bar and tube/profile forms.
- Rod / Round Bar / Flat Bar
- Tube/Profile